INSPIRE™ 136
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Braskem Europe GmbH |
| Trademark: | INSPIRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5dbKZP_INSPIRE-136.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INSPIRE™ 136 Performance Polymer is a low gel resin developed for the manufacturing of films for quality applications. INSPIRE 136 combines good processability with good stiffness and low gel content. INSPIRE 136 can be used as a blend partner to make more effective films with blown or cast film technology. Applications for INSPIRE™ 136 Performance Polymer:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.5 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus (Injection Molded) | 1150 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Film Puncture Energy (50 µm) | 3.00 | J | ASTM D5748 |
| Film Puncture Force (50 µm) | 70.0 | N | ASTM D5748 |
| Tensile Modulus | ISO 527-3 | ||
| 2% secant, MD : 50 µm, blown film | 680 | MPa | ISO 527-3 |
| 2% secant, TD : 50 µm, blown film | 650 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 50 µm, blown film | 27.0 | MPa | ISO 527-3 |
| TD : Yield, 50 µm, blown film | 23.0 | MPa | ISO 527-3 |
| MD : Broken, 50 µm, blown film | 35.0 | MPa | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 30.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | 610 | % | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 650 | % | ISO 527-3 |
| Dart Drop Impact (50 µm, Blown Film) | 170 | g | ISO 7765-1/A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm, blown film | 27 | g | ASTM D1922 |
| TD : 50 µm, blown film | 50 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1(0.45 MPa, Unannealed) | 88.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature 2 | 151 | °C | ISO 306/A |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 230 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件：模具间隙：1.0 mm熔体温度：230°C放大比：2.5:1 |
| Note Message | |
|---|---|
| 1 . | Injection Molding |
| 2 . | Injection Molding |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DOWLEX™ 2045 | The Dow Chemical Company | LLDPE | DOWLEX™ |
| Ecobarrier® 2612 | Noble Polymers | Polyolefin, Unspecified | Ecobarrier® |
| Karina IVORY PVC COMPOUND 70900-35/ 1-E-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina IVORY PVC COMPOUND -E 851-35/ 1-E-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PARAPET HR-G | Kuraray Co., Ltd. | Acrylic (PMMA) | PARAPET |