Braskem PE GP100BKXP
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5cqB9G_BraskemPEGP100BKXP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GP100BKXP is a High Density Polyethylene compound specially developed for the manufacturing of extruded pipes for water distribution. It is produced with bimodal technology and has high molar mass. It shows high mechanical properties and has excellent resistance to hydrostatic pressure and stress cracking. This resin has MRS (Minimum Required Strength) of 10 MPa, according to ISO 9080, and is classified as PE 100, according to ISO 12162. GP100BKXP contains carbon black that protects it against ultraviolet radiation action and photodegradation. Meets the requirements of NBR 15561:07 and ISO 4427:07. Application: Black PE 100 pressure pipes for water distribution, underwater emissaries and pressurized sewer systems; jacketing of underwater cables; pipes for mining. Process: Pipe Extrusion. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.958 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 0.25 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 2.00 mm, 10% Igepal, Compression Molded, F50) | > 1000 | hr | ASTM D1693 |
| Carbon Black Content | 2.0 - 2.5 | % | ASTM D1603 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 65 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, molding | 25.0 | MPa | ASTM D638 |
| Fracture, molding | 40.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, molding | 10 | % | ASTM D638 |
| Fracture, molding | 1500 | % | ASTM D638 |
| Flexural Modulus - 1% Secant (Compression Molded) | 1090 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, Compression Molded) | 68.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 125 | °C | ASTM D1525 1 |
| Note Message | |
|---|---|
| 1 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenac™-C TFC77 | Asahi Kasei Chemicals Corporation | Acetal (POM) Copolymer | Tenac™-C |
| TECATRON™ GF40 | Ensinger Inc. | PPS | TECATRON™ |
| 4PROP® 9C22430 | 4Plas | PP Copolymer | 4PROP® |
| Chemlon® 115 GH | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Deco-Coat™ 60-7180 | Epoxies, Etc. | Acrylic, Unspecified | Deco-Coat™ |