Ad-Tech Epoxy EL-337
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Ad-Tech Plastic Systems Corp. |
| Trademark: | Ad-Tech Epoxy |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5cWOhu_Ad-Tech-Epoxy-EL-337.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EL-337 is an improved, health-safe, two component, filled, non-staining, high temp epoxy laminating system specifically developed for room temp hardening (B Stage) with high temp properties for high temp tooling applications. EL-337 has excellent handling properties and fabric wet-out to produce a void free tool with high dimensional stability. EL-337 can be used in the construction of large or small tools, as well as production parts. El-337 can also be used with ADTECH High Temp Surface Coats ES-219 and ES-229. Tools made with EL-337 can be used at continuous temperature of 160°C/320°F, and intermittent temperatures up to 191°C/375°F. While EL-337 will gel at room temp, it must be post-cured to achieve ultimate strength. The system contains no MDA or VCHD. Typical applications include: vacuum form molds, prototype injection molds, high temp bonding fixtures, spray metal molds, compression molds, high temp laminated molds and parts to be used in high temp applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Density | 1.26 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow | 0.13 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 88 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 188 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 1.6 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| -- 2 | 8960 | MPa | |
| 149°C | 5650 | MPa | |
| Flexural Strength | ASTM D790 | ||
| -- 3 | 269 | MPa | |
| Break, 149°C | 58.5 | MPa | |
| Compressive Strength 4 | 103 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact - Cast Bar | 0.598 | J |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Work Time 5 | 45.0 to 60.0 | min |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 114 | °C | ASTM E1356 |
| CLTE - Flow | 4.3E-5 | cm/cm/°C | ASTM D696 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 1.0 Mix Ratio by Weight: 16 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 4.9 | ||
| Shelf Life (25°C) | 100 | wk | |
| Thermoset Mix Viscosity (25°C) | 3000 to 5000 | cP | ASTM D2393 |
| Demold Time (25°C) | 960 to 1400 | min | |
| Post Cure Time | 72 to 120 | hr |
| Note Message | |
|---|---|
| 1 . | 6 Layer, 10 Ounce Glass Fabric Laminate |
| 2 . | 6 Layer, 10 Ounce Glass Fabric Laminate |
| 3 . | 6 Layer, 10 Ounce Glass Fabric Laminate |
| 4 . | Cast Bar |
| 5 . | 232g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMOFIN PPC342M6 | Polyram Ram-On Industries | PP Copolymer | RAMOFIN |
| Ultrathene® UE637000 | LyondellBasell Industries | EVA | Ultrathene® |
| Ad-Tech Epoxy ES-204-SC | Ad-Tech Plastic Systems Corp. | Epoxy | Ad-Tech Epoxy |
| BP Flex A 0285 BLK | Buckeye Polymers, Inc. | TPE | BP Flex |
| Ebalta SG 700 / PUR 5 | Ebalta Kunststoff GmbH | PUR, Unspecified | Ebalta |