| PA 6-Copolymer, 15 % glass fibers, injection molding, improved impact strength, heat-aging stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.17 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.60 | -- | g/cm³ | ISO 60 |
| Molding Shrinkage | ISO 2577 | |||
| Across Flow : 280°C, 2.00 mm 1 | 0.80 | -- | % | |
| Across Flow : 120°C, 4 hr, 2.00 mm 2 | 0.10 | -- | % | |
| Flow : 280°C, 2.00 mm 3 | 0.50 | -- | % | |
| Flow : 120°C, 4 hr, 2.00 mm 4 | 0.10 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 7.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.0 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 120 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 4300 | 2100 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 85.0 | 55.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 4.5 | 15 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 4000 | 2000 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | |||
| 3.5% Strain, 23°C | 120 | 55.0 | MPa | |
| 23°C 6 | 135 | 70.0 | MPa | |
| Flexural Strain at Flexural Strength 7(23°C) | 5.5 | 8.0 | % | ISO 178/A |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6/66-HI, GHR, 14-040, GF15 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 to 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 10 | 10 | kJ/m² | |
| 23°C | 20 | 35 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 80 | 80 | kJ/m² | |
| 23°C | 70 | 110 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | 10 | 10 | kJ/m² | |
| 23°C | 20 | 35 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 65 | 60 | kJ/m² | |
| 23°C | 60 | 90 | kJ/m² | |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | |||
| -30°C | 4.00 | -- | J | |
| 23°C | 10.0 | -- | J | |
| Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | |||
| -30°C | 750 | -- | N | |
| 23°C | 1500 | -- | N |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 200 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 175 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 200 | -- | °C | ISO 306/B120 |
| Melting Temperature 8 | 214 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C | 4.0E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 1.5E-4 | -- | cm/cm/°C |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vinylbond 95-950-65 | Colorite Polymers | PVC, Flexible | Vinylbond |
| AQUATUF® HMP-337 (Roto) | Ravago Manufacturing Americas, LLC | HDPE | AQUATUF® |
| ExxonMobil™ LDPE EVA Copolymers LD 364HE | ExxonMobil Chemical | LDPE | ExxonMobil™ LDPE |
| LNP™ THERMOCOMP™ RF006XXH compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| Hifax TRS 123D NAT | LyondellBasell Industries | TPO (POE) | Hifax |