Starex GR-4017
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5cLKV6_Starex-GR-4017.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starex GR-4017 is an Acrylonitrile Butadiene Styrene (ABS) product filled with glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 17 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 to 0.40 | % | ASTM D955 |
| Ash Content | 17 | % | ISO 3451 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 117 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5200 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 1 | 77.0 | MPa | ASTM D638 |
| Yield | 93.0 | MPa | ISO 527-2/50 |
| Break | 93.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 2 | 5000 | MPa | ASTM D790 |
| -- 3 | 5800 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 120 | MPa | ASTM D790 |
| -- 5 | 131 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 6(23°C) | 8.6 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 6.35 mm | 79 | J/m | ASTM D256 |
| 23°C 7 | 8.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 4.00 mm | 105 | °C | ISO 75-2/B |
| 0.45 MPa, Annealed | 109 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 100 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 100 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed, 4.00 mm | 105 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 105 | °C | ISO 306/B50 |
| -- | 107 | °C | ISO 306/B120 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 | °C | |
| Desiccant Dryer | 80.0 | °C | |
| Drying Time | |||
| -- | 4.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 230 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 250 to 260 | °C | |
| Nozzle Temperature | 260 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Pressure | 93.2 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 2.8 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | Thickness: 4 mm |
| 7 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| QR Resin QR-1015 | QTR, Inc. | PC | QR Resin |
| Bergamid™ A70 G30 Black | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Estane® ZHF 90AT0 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Estane® |
| Fainplast PVC CKL 84/3 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| OTECH PVC OW140 - Cable Jacket | OTECH Corporation | PVC, Unspecified | OTECH PVC |