MAXAMID™ RC66-BK09
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Pier One Polymers, Inc. |
| Trademark: | MAXAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5cL33N_MAXAMID-RC66-BK09.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MAXAMID™ RC66 is available in natural and custom colors, internal and external lubricants, UV stabilized and other modifications. Manufactured with recycled content. Further information and details are available upon request. |
| General Information | |
|---|---|
| Recycled Content |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 75.9 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 20 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2760 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 121 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 235 | °C | ASTM D648 |
| Peak Melting Temperature | 255 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Moisture | < 0.20 | % | |
| Processing (Melt) Temp | 290 to 305 | °C | |
| Mold Temperature | 38.0 to 93.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1385 D | RTP Company | PPS | RTP |
| PRIMALENE WPP694M | Southern Polymer, Inc. | mLLDPE | PRIMALENE |
| TECHNYL® C 30H1 V30 NATURAL/F | Solvay Engineering Plastics | Nylon 6 | TECHNYL® C |
| APEX® RE 8118 | Teknor Apex Company | PVC, Rigid | APEX® |
| Hylon® N1000L2 | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |