Silopren® LSR 2610

Category:	Silicone Rubber, LSR , Silicone Rubber, LSR
Manufacturer:	Momentive Performance Materials Inc.
Trademark:	Silopren®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	5cGWGY_Silopren-LSR-2610.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Silopren LSR 2610 is a two-component liquid silicone rubber for injection moulding processes. Silopren LSR 2610 shows in comparison to Silopren LSR 2010 a lower viscosity, improved tear resistance and a higher reactivity. Therefore, it is also possible to reduce the vulcanisation temperature while maintaining a standard crosslinking rate. The increased reactivity does not affect the properties of the vulcanisate.

Key Features and Benefits
Vulcanisates consisting of Silopren LSR 2610 are distinguished by the following properties:

high reactivity, lower viscosity, shorter cycle time

excellent thermal stability

high stability and flexibility at low temperatures

good rubber-like properties, high tear resistance

high stability to ozone and ultraviolet light

outstanding resistance to ageing,

excellent dielectric behaviour over a wide range of temperatures,

not readily combustible, does not melt or drip

easy pigmentable with the LSR Colour Pastes

Potential Applications
Because of the outstanding properties Silopren LSR 2610 is particularly suitable for the following elastomeric articles: stoppers, vibration dampers, shoe inserts s.o.

General Information
Features	Fast Cure Fast Molding Cycle Good Colorability Good Mold Release Good Stability Good Tear Strength Good Thermal Stability Good UV Resistance High Reactivity Low Temperature Flexibility Low Viscosity Ozone Resistant Vibration Damping
Uses	Footwear
Forms	Liquid
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	1.04	g/cm³	DIN 53479

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	16		DIN 53505

Elastomers	Nominal Value	Unit	Test Method
Tensile Strength	2.90	MPa	DIN 53504
Tensile Elongation (Break)	560	%	DIN 53504
Tear Strength ¹	18.0	kN/m	ASTM D624
Compression Set (175°C, 22 hr)	12	%	DIN 53517

Thermoset	Nominal Value	Unit	Test Method
Thermoset Components
Part A	Mix Ratio by Weight: 1.0
Part B	Mix Ratio by Weight: 1.0
Post Cure Time (200°C)	4.0	hr

Additional Information	Nominal Value	Unit	Test Method
Vulcanization (175°C)	10.0	min

Uncured Properties	Nominal Value	Unit	Test Method
Color
-- ²	Translucent
-- ³	Translucent
Viscosity			DIN 53018
20°C ⁴	67	Pa·s
20°C ⁵	90	Pa·s
Pot Life (20°C)	4300	min

Note Message
1 .	Die B
2 .	Part B
3 .	Part A
4 .	Part B
5 .	Part A

Resin Grade	Manufacturer	Category	Trademark
RTP 200 GB 10 TFE 10	RTP Company	Nylon 66	RTP
Matrixx 50S5202	The Matrixx Group, Inc.	PC	Matrixx
TAISOX 7470M	Formosa Plastics Corporation	EVA	TAISOX
Tisoplen® PPC 10 MNF TALC	Tisan	PP Copolymer	Tisoplen®
Elastron® G G100.A90.N	Elastron USA, Inc.	SEBS	Elastron® G