AVALON® 80 ABU

Category: TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester)
Manufacturer: Huntsman Corporation
Trademark: AVALON®
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: 5bcYrb_AVALON-80-ABU.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
AVALON 80 ABU is a high performance polyester based thermoplastic polyurethane for injection moulding.

AVALON 80 ABU is part of the AVALON Perform Range and offers a premium soling material for the sporting goods and fashion markets and is supplied with a high degree of stabilisation against premature yellowing from sunlight.

The features offered include:
  • UV resistance
  • Excellent surface definition
  • Abrasion resistance
  • Flex resistance
  • Phthalate free TPU
General Information
Features
  • Good UV resistance
  • Good wear resistance
  • Excellent appearance
Uses
  • Sporting goods
  • Footwear
Forms
  • Particle
Processing Method
  • Injection molding
PhysicalNominal ValueUnitTest Method
Density 1.20g/cm³ISO 2781
HardnessNominal ValueUnitTest Method
Durometer Hardness ISO 868
    Shaw A 80ISO 868
    Shaw D 30ISO 868
MechanicalNominal ValueUnitTest Method
Flexural Modulus (23°C)25.0MPaISO 178
Ross Flex 1(-10°C)2.5E+5Cycles
Abrasion Resistance 35.0mm³ISO 4649
ElastomersNominal ValueUnitTest Method
Tensile Stress ISO 37
    100% strain 5.00MPaISO 37
    300% strain 13.0MPaISO 37
Tensile Stress (Break)30.0MPaISO 37
Tensile Elongation (Break)500%ISO 37
Tear Strength 295kN/mISO 34-1
Compression Set (23°C)20%ISO 815
Additional Information
Test plates conditioned 20 hours at 100°C before testing
InjectionNominal ValueUnit
Drying Temperature - Desiccant Dryer 80.0 - 90.0°C
Drying Time - Desiccant Dryer 2.0hr
Hopper Temperature 25.0 - 35.0°C
Rear Temperature 190 - 200°C
Middle Temperature 195 - 205°C
Front Temperature 200 - 210°C
Nozzle Temperature 185 - 195°C
Mold Temperature 25.0 - 50.0°C
Injection Pressure 2.00 - 10.0MPa
Injection Rate Slow
Holding Pressure 1.00 - 5.00MPa
Back Pressure 0.0300 - 0.300MPa
Screw Speed 20 - 80rpm
Screw L/D Ratio 20.0:1.0 to 25.0:1.0
Screw Compression Ratio 2.0 : 1.0 - 3.0 : 1.0
Injection instructions
Typical Screw Diameter : 40 - 120 mm3 Stage Design Feed Zone : 0.4L Compression Zone : 0.3L Metering Zone : 0.3L
Note Message
1 .BS 5131
2 .Method B, right-angle specimen (without cut)
Resin Grade Manufacturer Category Trademark
UNIPA® Rg Nytef Plastics, Ltd. Nylon 66 UNIPA®
Clear Cote™ POLY-U-FOAM™ 4 lb Urethane Foam System Club Kit, Inc. PUR, Unspecified Clear Cote™
EASYPOXY® K-230 Cytec Industries Inc. Epoxy EASYPOXY®
LOXIM 820 01 HB LOXIM Industries Private Limited PP, Unspecified LOXIM
Exceed™ XP 8656ML ExxonMobil Chemical PP Elastomer Exceed™ XP