Category: | Nylon 6 , Polyamide 6 |
Manufacturer: | Grupo Repol |
Trademark: | DINALON® |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | 5bDXqU_DINALON-B2S35-V2-7035.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
RAL 7035 |
General Information | |
---|---|
Features |
|
Appearance |
|
Forms |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Density | 1.16 | g/cm³ | ISO 1183/A |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Modulus | 3300 | MPa | ISO 527-2 |
Tensile Stress (Break) | 75.0 | MPa | ISO 527-2 |
Tensile Strain (Yield) | 4.0 | % | ISO 527-2 |
Flexural Modulus | 1800 | MPa | ISO 178 |
Flexural Stress | 80.0 | MPa | ISO 178 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Charpy Notched Impact Strength (23°C) | 3.0 | kJ/m² | ISO 179/1eA |
Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Heat Deflection Temperature (1.8 MPa, Unannealed) | 55.0 | °C | ISO 75-2/A |
Vicat Softening Temperature | 200 | °C | ISO 306/B |
Flammability | Nominal Value | Test Method | |
---|---|---|---|
Flame Rating | V-2 | UL 94 |
Additional Information |
---|
Humidity, Karl-Fisher, ISO 15512/A: <0.25%Vicat Softening Temperature, ISO 306, 50N: >200°C |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
POYAD SB131 | Pooya Polymer Tehran | PP, Unspecified | POYAD |
NEXUS PE HDPE-753 | Nexus Resin Group, LLC. | HDPE | NEXUS PE |
NEOFLON™ EPW-1606BL | DAIKIN AMERICA, INC. | ETFE | NEOFLON™ |
Beamset AQ-17 | Arakawa Chemical Industries, Ltd. | PUR, Unspecified | Beamset |
Diofan® 193 D | Solvay Specialty Polymers | PVDC | Diofan® |