Complet® LCF15-LGF35-PA66
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PlastiComp, Inc. |
| Trademark: | Complet® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5bCvMM_Complet-LCF15-LGF35-PA66.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Complet®LCF15-LGF35-PA66 is a polyamide 66 (nylon 66) product, which contains 35% long glass fibers and 15% long carbon fibers. It is available in North America, Europe or Asia Pacific. The main features are: Rohs certification. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.54 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 23400 | MPa | ASTM D638 |
| Tensile Strength | 269 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.0 - 2.0 | % | ASTM D638 |
| Flexural Modulus | 17200 | MPa | ASTM D790 |
| Flexural Strength | 386 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 320 | J/m | ASTM D256 |
| Unnotched Izod Impact | 960 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 254 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.18 | % | |
| Suggested Max Regrind | 5 | % | |
| Rear Temperature | 282 - 299 | °C | |
| Middle Temperature | 288 - 304 | °C | |
| Front Temperature | 293 - 310 | °C | |
| Nozzle Temperature | 288 - 304 | °C | |
| Processing (Melt) Temp | 293 - 310 | °C | |
| Mold Temperature | 93.3 | °C | |
| Back Pressure | 0.172 - 0.345 | MPa | |
| Screw Speed | 30 - 50 | rpm | |
| Cushion | 6.35 | mm | |
| Screw L/D Ratio | 18.0:1.0 to 20.0:1.0 | ||
| Screw Compression Ratio | 2.0 : 1.0 - 3.0 : 1.0 |
| Injection instructions |
|---|
| Injection speed: 2 to 3 in/secInjection pressure: medium to maximum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx CPP5B30 | The Matrixx Group, Inc. | PP Copolymer | Matrixx |
| Mecoline I RDX 5244 F | Melos GmbH | Fluorelastomer | Mecoline |
| Hy-Vin® XN77970 | INEOS Compounds | PVC, Flexible | Hy-Vin® |
| Monprene® CE-922968 (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |
| Sylvin 8393-93C Natural | Sylvin Technologies Incorporated | PVC, Semi-Rigid | Sylvin |