RTP 200A SI 2 Z
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5aucgX_RTP-200A-SI-2-Z.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.3 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 1.9 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3100 | MPa | ASTM D638 |
| Tensile Strength | 82.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 75 | % | ASTM D638 |
| Flexural Modulus | 2410 | MPa | ASTM D790 |
| Flexural Strength | 96.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 1600 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 171 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 71.1 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+11 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm, RTP Tested) | V-2 | UL 94 |
| Additional Information |
|---|
| Molding Shrinkage, ASTM D955, .25in: 0.017 in/in |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 232 - 288 | °C | |
| Middle Temperature | 232 - 288 | °C | |
| Front Temperature | 232 - 288 | °C | |
| Mold Temperature | 65.6 - 93.3 | °C | |
| Injection Pressure | 68.9 - 138 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 7990E | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| Vibrathane® 6007 | Chemtura | PUR-Ester/TDI | Vibrathane® |
| ESTABLEND 6600 | Cossa Polimeri S.r.l. | ASA+PC | ESTABLEND |
| Karina YELLOW PVC COMPOUND 701D02/ 23-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUBAN™ 1102 KQH | Oman Oil Refineries & Petroleum Indistries Co. (Orpic) | PP Homopolymer | LUBAN™ |