DIAMALOY ABSPC 754M
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Network Polymers, Inc. |
| Trademark: | DIAMALOY ABSPC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5aWG5t_DIAMALOY-ABSPC-754M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Diamaloy ABSPC 754M- Medical Grade resin is a non-reinforced, flame retardant, antimony-, bromine-, and chlorine free. Diamaloy ABSPC 754M is naturally opaque and is available in custom colors. High heat and impact resistance. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 1(265°C/5.0 kg) | 30 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.40 to 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 2(Injection Molded) | 2410 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield 3 | 55.8 | MPa | |
| Break | 52.1 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield 4 | 5.1 | % | |
| Break | 140 | % | |
| Flexural Modulus 5 | 2280 | MPa | ASTM D790A |
| Flexural Strength 6(Yield, Injection Molded) | 82.7 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 750 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 96.1 | °C | ASTM D648 |
| Vicat Softening Temperature | 122 | °C | ASTM D1525 7 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 93.3 | °C | |
| Drying Time - Desiccant Dryer | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 221 to 232 | °C | |
| Middle Temperature | 227 to 235 | °C | |
| Front Temperature | 249 to 260 | °C | |
| Nozzle Temperature | 249 to 263 | °C | |
| Mold Temperature | 65.6 to 79.4 | °C |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | Type I |
| 3 . | Type I, 51 mm/min |
| 4 . | Type I, 51 mm/min |
| 5 . | Method I (3 point load), 1.3 mm/min |
| 6 . | Method I (3 point load) |
| 7 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECAMID™ HS | Ensinger Inc. | Nylon 66 | TECAMID™ |
| Mylar® EC (300 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| Infino GW-1030S | SAMSUNG SDI CO., LTD. | PC | Infino |
| Karina STRAW CPVC COMPOUND 790-38/23-CRPC (**) | Karina Ind. e Com. de Plásticos Ltda | CPVC | Karina |
| LNP™ LUBRILOY™ UX98388 compound | SABIC Innovative Plastics | PPA | LNP™ LUBRILOY™ |