Devcon Aluminum Liquid (F-2)
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Devcon |
| Trademark: | Devcon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5ZddMz_Devcon-Aluminum-Liquid-F-2-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Aluminum-filled, pourable epoxy for making molds, patterns, and holding fixtures that can be machined, drilled, or tapped. Intended Use:
Product features:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.58 | g/cm³ | |
| Specific Volume | 0.632 | cm³/g | |
| Solid content- by Volume | 100 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Temperature Resistance | |||
| Dry | 121 | °C | |
| Wet | 49 | °C | |
| Tensile Shear Adhesion | 18.6 | MPa | ASTM D1002 |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 0.090 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 85 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5170 | MPa | ASTM D638 |
| Flexural Strength | 49.5 | MPa | ASTM D790 |
| Compressive Strength | 67.7 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.66 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 3.9 | kV/mm | ASTM D149 |
| Dielectric Constant | 8.60 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mixing ratio by weight: 9.0 Mixing ratio by capacity: 5.0 | ||
| Component B | Mixing ratio by weight: 1.0 Mixing ratio by capacity: 1.0 | ||
| Pot Life (24°C) | 75 | min | |
| Thermoset Mix Viscosity | 15000 - 25000 | cP |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cured 7 days @ 75°F |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Curing Time | 16 | hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEXUS Reprocessed HIPS 8/2 RBK | Nexus Resin Group, LLC. | PS (HIPS) | NEXUS Reprocessed |
| CERTENE™ LDF-820A | Muehlstein | LDPE | CERTENE™ |
| Geon™ Vinyl Rigid Extrusion LR610 white 1046 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| Hifax CA 1110 G4 LS 1740 | LyondellBasell Industries | PP Copolymer | Hifax |
| Sylvin 8215-80 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |