PrimaFlex® HI 0302
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Plastic Solutions, Inc. |
| Trademark: | PrimaFlex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5Z0nms_PrimaFlex-HI-0302.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Description: HI 0302 is a high impact polystyrene designed specifically for extrusion and thermoforming. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 3.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2070 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 24.8 | MPa | ASTM D638 |
| Flexural Modulus | 2210 | MPa | ASTM D790 |
| Flexural Strength | 47.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 120 | J/m | ASTM D256 |
| Gardner Impact | 12.4 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 94.4 | °C | ASTM D648 |
| Vicat Softening Temperature | 102 | °C | ASTM D1525 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Versaflex™ OM 6258-1 | PolyOne Corporation | TPE | Versaflex™ |
| Zeoforte® ZSC 2195LCX | Zeon Chemicals L.P. | NBR | Zeoforte® |
| Alathon® M6028 | LyondellBasell Industries | HDPE | Alathon® |
| Ipethene® 320 | Carmel Olefins Ltd. | LDPE | Ipethene® |
| Karina GRAY PVC COMPOUND 801-18/489-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |