InnoPlus LD2420H
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | PTT Global Chemical Public Company Limited |
| Trademark: | InnoPlus |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5YeyoC_InnoPlus-LD2420H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Special Characteristics: InnoPlus LD2420H is produced by high pressure tubular process, a technology licensed by LyondellBasell. This grade offers easy processability, excellent optical property and low gel level. Typical Applications: InnoPlus LD2420H is a very versatile of general purpose films, shrink films, food packaging films and foam applications. Additives: No additives. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.9 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Compression Molded) | 260 | MPa | ISO 527-2 |
| Tensile Stress (Yield, Compression Molded) | 11.0 | MPa | ISO 527-2 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Break, 50 µm, Blown Film | 21.0 | MPa | |
| TD : Break, 50 µm, Blown Film | 20.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 50 µm, Blown Film | 250 | % | |
| TD : Break, 50 µm, Blown Film | 600 | % | |
| Dart Drop Impact (50 µm, Blown Film) | 90 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 93.0 | °C | ASTM D1525 |
| Melting Temperature | 111 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 50.0 µm, Blown Film) | > 80 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | < 8.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 to 200 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Styrolux® 684D | INEOS Styrolution Group GmbH | SBC | Styrolux® |
| ELIX™ ABS H607AS | ELIX Polymers, S. L. | ABS | ELIX™ ABS |
| Emulprene® 1502 | INSA | SBR, Emulsion | Emulprene® |
| Karina COMP. PVC BROWN 732-36/563-W-ERB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Petrotene® PP A3 T40 PRTA011 PH359 | Petropol Industry and Trade of Polymers LTDA | PP Homopolymer | Petrotene® PP |