Sup-tech B101
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Shanghai Suptech Engineering Plastics Co. Ltd. |
| Trademark: | Sup-tech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5YSufx_Sup-tech-B101.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sup-tech B101 is a Polyamide 6 (Nylon 6) product. It can be processed by injection molding and is available in Asia Pacific. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | DIN 53479 |
| Molding Shrinkage | 1.0E-3 to 0.014 | % | DIN 53464 |
| Water Absorption | DIN 53495 | ||
| 23°C, 24 hr | 1.8 | % | |
| Saturation, 23°C | 8.5 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 72.0 | MPa | DIN 53455 |
| Tensile Strain (Break) | 80 | % | DIN 53452 |
| Flexural Modulus | 2500 | MPa | DIN 53457 |
| Flexural Stress | 90.0 | MPa | DIN 53457 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 6.0 | kJ/m² | DIN 53453 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | DIN 53461 | ||
| 0.45 MPa, Unannealed | 160 | °C | |
| 1.8 MPa, Unannealed | 62.0 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Electric Strength | 20 | kV/mm | DIN 53481 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 230 to 265 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® W38S2 | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| Spartech Polycom SC1-5007 | Spartech Polycom | ABS | Spartech |
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 4212 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |
| EMERGE™ PC 8702-15 (EU) | Trinseo | PC | EMERGE™ |
| POCAN® B 7616 000000 | LANXESS Corporation | PC+PBT | POCAN® |