Starpylen HU 30E4 ECR
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Starpylen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5WTrFM_Starpylen-HU-30E4-ECR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starpylen HU 30E4 ECR is a reinforced Polypropylene with a low carbon footprint renewable mineral filler, Injection Molding Resin (also known as HU30E4ECR). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (4.00 mm) | 1.8 to 2.0 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 28.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 8.0 | % | ISO 527-2 |
| Flexural Modulus | 2100 | MPa | ISO 178 |
| Flexural Stress | 41.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 1(23°C) | 3.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 2(23°C) | 15 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed, 64.0 mm Span) | 61.0 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 190 to 200 | °C | |
| Middle Temperature | 190 to 200 | °C | |
| Front Temperature | 190 to 200 | °C | |
| Processing (Melt) Temp | 190 to 200 | °C | |
| Mold Temperature | 30.0 to 50.0 | °C |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® A9855A | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| SPESIN® KP212G30V0BM | Kolon Plastics, Inc. | PBT | SPESIN® |
| Bergamid™ A70 G5 T | PolyOne Corporation | Nylon 66 | Bergamid™ |
| HiFill® TPU/I CF10 | Techmer Engineered Solutions | TPU-Polyether | HiFill® |
| LNP™ THERMOCOMP™ PF00DS-BK1G298 compound | SABIC Innovative Plastics Europe | Nylon 6 | LNP™ THERMOCOMP™ |