UmaPET MHLO

Category:	PET , Polyethylene Terephthalate
Manufacturer:	Ester Industries Ltd.
Trademark:	UmaPET
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	5W5zw4_UmaPET-MHLO.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

KEY FEATURES

UmaPET MHLO film is medium Haze, medium gloss film with excellent muted and grainy surface with one side chemically primed for improved adhesion performance.

The film exhibits excellent thermal, mechanical and matte surface properties along with excellent dimensional stability and excellent process ability.

After metallization, shows silver finish as aesthetic.

APPLICATIONS

The film is widely used for label face stocks, carrier for thermal transfer printing, hot stamping, paper board and carton lamination applications.

Chemical coated surface gives enhanced adhesion performance to inks, adhesives and other primer coatings and metal in metallization.

Metallized films can be used as label face stocks and sandwich barrier layer which showssilver aesthetic appearance to the package in flexible packaging.

General Information
Features	Excellent Printability Good Adhesion Good Dimensional Stability Good Processability Medium Gloss Metallizable
Uses	Coating Applications Film Labels Laminates
Appearance	Matte Finish
Forms	Film

Physical	Nominal Value	Unit	Test Method
Molding Shrinkage			ASTM D1204
Flow : 150°C, 30 min, 0.0120 mm	2.0	%
Across Flow : 150°C, 30 min, 0.0120 mm	0.40	%

Mechanical	Nominal Value	Unit	Test Method
Coefficient of Friction ¹			ASTM D1894
vs. Itself - Dynamic	0.38
vs. Itself - Static	0.45

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	12	µm
Film Thickness - Recommended / Available	12 µm
Tensile Strength			ASTM D882
MD : Break, 12 µm	186	MPa
TD : Break, 12 µm	196	MPa
Tensile Elongation			ASTM D882
MD : Break, 12 µm	90	%
TD : Break, 12 µm	85	%
Yield (12.0 µm)	59.5	m²/kg	Internal Method

Additional Information	Nominal Value	Unit	Test Method
Wetting Tension - Coated side (12.0 µm)	48	dyne/cm	ASTM D2578

Optical	Nominal Value	Unit	Test Method
Gloss (60°)	48		ASTM D2457
Haze (12.0 µm)	44	%	ASTM D1003

Note Message
1 .	12 µm

Resin Grade	Manufacturer	Category	Trademark
Mirakutoran® TPU E890PBOO	Japan Mirakutoran Inc.	TPU Alloy	Mirakutoran® TPU
SILVER® PA540N	Guangdong Silver Age Sci & Tech. Co., Ltd	Nylon 6	SILVER®
Desmopan® DP 6072A	Covestro - PUR	TPU, Unspecified	Desmopan®
Latimass 62-01 D025	LATI S.p.A.	Nylon 6	Latimass
Karina WHITE PVC COMPOUND TR-651-10/133-B-IS	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina