Bergamid™ A70 G35 U BK TM-X SO3
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Bergamid™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5W4slu_Bergamid-A70-G35-U-BK-TM-X-SO3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 6616064 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.48 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1(23°C, 4.00 mm) | 0.30 to 0.50 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C, 4.00 mm) | 11000 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C, 4.00 mm) | 150 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C, 4.00 mm) | > 2.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 6.0 | kJ/m² | |
| 23°C | 8.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C, Injection Molded | 46 | kJ/m² | |
| 23°C | 65 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed | 260 | °C | ISO 75-2/B |
| 1.8 MPa, Annealed | 250 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm, ALL | V-0 | ||
| 3.20 mm, ALL | V-0 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.800 mm | 960 | °C | |
| 3.00 mm | 960 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 65.0 to 85.0 | °C |
| Note Message | |
|---|---|
| 1 . | Mold Shrinkage on Tensile Bar, flowBergamnn Method |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 501 BLACK | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| BESTNYL SE10VI02AU | Triesa Plastics | Nylon 66 | BESTNYL |
| Colorite Rigid PVC 2101 | Colorite Polymers | PVC, Rigid | Colorite Rigid PVC |
| EZPrene 9575A SHF | ENPLAST Americas, a Ravago Group Company | TPV | EZPrene |
| Hifax TYC337P 2 | LyondellBasell Industries | Polyolefin, Unspecified | Hifax |