Fibremod™ GE277AI
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Fibremod™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5VswBV_Fibremod-GE277AI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Fibremod GE277AI is a 20 % chemically coupled high performance glass fibre reinforced polypropylene compound intended for injection moulding. This material has an excellent balance between impact strength and stiffness and is easy to process. The product is available in standard black 9502. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (1.00 mm) | 4900 | MPa | ISO 527-2 |
| Tensile Stress | 85.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus 1 | 4200 | MPa | ISO 178 |
| Flexural Stress | 107 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 9.5 | kJ/m² | ISO 179/1eA |
| 23°C | 11 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 52 | kJ/m² | ISO 179/1eU |
| 23°C | 50 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 142 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 120 | °C | ISO 306/B |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Fogging 2(100°C) | mg | DIN 75201 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Emission | µgC/g | VDA 277 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 30.0 - 70.0 | °C | |
| Holding Pressure | 30.0 - 70.0 | MPa |
| Injection instructions |
|---|
| Feeding Temperatrue: 40 - 80 °CMass Temperature: 220 - 260 °CBack Pressure: Low to MediumScrew Speed: Low to MediumFlow Front Speed: 100 - 200 mm/s |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 16 h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TF7STE (Series: FC/CS) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Gallonprene® GP540-8005 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Karina CLEAR PVC COMPOUND -E 80/230-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lupoy® HP5004 | LG Chem Ltd. | PC+ABS | Lupoy® |
| Petrothene® GA694189 | LyondellBasell Industries | LLDPE | Petrothene® |