TECHNYL® C 236SI BLACK
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5Vb9Ms_TECHNYLC236SIBLACK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL® C 236SI Black is an unreinforced polyamide 6, with high impact resistance, for injection moulding. This grade offers high impact strength and flexibility. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.09 | -- | g/cm³ | ISO 1183/A |
| Water Absorption (23°C, 24 hr) | 1.3 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 2200 | 910 | MPa | ISO 527-2/1A |
| Tensile Stress | ISO 527-2/1A | |||
| Yield, 23°C | 54.0 | -- | MPa | ISO 527-2/1A |
| Fracture, 23°C | 47.0 | 42.0 | MPa | ISO 527-2/1A |
| Tensile Strain | ISO 527-2 | |||
| Yield, 23°C | 4.0 | -- | % | ISO 527-2 |
| Fracture, 23°C | 55 | -- | % | ISO 527-2 |
| Flexural Modulus (23°C) | 1930 | 640 | MPa | ISO 178 |
| Flexural Stress (23°C) | 77.0 | 28.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 16 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 76 kJ/m² | No Break | ISO 179/1eA | |
| Charpy Unnotched Impact Strength (23°C) | No Break | -- | ISO 179/1eU | |
| Notched Izod Impact (23°C) | 66 | -- | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 56.0 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 220 | -- | °C | ISO 11357-3 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 240 - 260 | °C | |
| Middle Temperature | 250 - 270 | °C | |
| Front Temperature | 260 - 280 | °C | |
| Mold Temperature | 70 - 90 | °C |
| Injection instructions |
|---|
| The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: For unfilled polyamide, Solvay recommends the use of high alloy steel with a weak chromium content. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris ABS LHF491I | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| Axiall PVC 9246 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| LGH 301 | LG Polymers India Pvt. Ltd. | PS (HIPS) | LGH |
| Plexar® PX2220 | LyondellBasell Industries | HDPE | Plexar® |
| Polidiemme® G/430 | Solvay Specialty Polymers | TSE | Polidiemme® |