VALOX™ ENH3500 resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5UGUti_VALOX-ENH3500-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unfilled PBT, Non-Brominated & Non-Chlorinated Flame Retardant |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 20.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 1.8 to 2.8 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 3150 | MPa | ASTM D638 |
| -- | 3200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 44.0 | MPa | ASTM D638 |
| Yield | 39.0 | MPa | ISO 527-2/50 |
| Break 4 | 42.0 | MPa | ASTM D638 |
| Break | 38.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 5 | 3.0 | % | ASTM D638 |
| Yield | 3.0 | % | ISO 527-2/50 |
| Break 6 | 10 | % | ASTM D638 |
| Break | 8.0 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 7 | 2750 | MPa | ASTM D790 |
| -- 8 | 2700 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 70.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 9 | 77.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 40 | J/m | ASTM D256 |
| -30°C 10 | 5.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 5.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 60.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 60.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 170 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| RTI Elec | 150 | °C | UL 746 |
| RTI Imp | 95.0 | °C | UL 746 |
| RTI Str | 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 4 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40.0 to 60.0 | °C | |
| Rear Temperature | 230 to 240 | °C | |
| Middle Temperature | 235 to 250 | °C | |
| Front Temperature | 240 to 260 | °C | |
| Nozzle Temperature | 230 to 255 | °C | |
| Processing (Melt) Temp | 245 to 260 | °C | |
| Mold Temperature | 40.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 5.0 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | Type I, 50 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zythane® 6085AU | Alliance Polymers & Services | TPU-Polyether | Zythane® |
| ArgoGUARDSelect™ 49510-60DV-AM | Argotec LLC | TPU, Unspecified | ArgoGUARDSelect™ |
| Jam HDPE HM9450F | Jam Petrochemical Company | HDPE | Jam HDPE |
| Karina IVORY PVC COMPOUND 837-35/1-E-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Polene LDPE D 2024 | TPI Polene Public Company Limited | LDPE | Polene LDPE |