InnoPlus LD2426K
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | PTT Global Chemical Public Company Limited |
| Trademark: | InnoPlus |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5UAKaT_InnoPlus-LD2426K.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| InnoPlus LD2426K is produced by high pressure tubular process, a technology licensed by LyondellBasell. This grade has well balance property of optical property, mechanical property and processability. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Compression Molded) | 260 | MPa | ISO 527-2 |
| Tensile Stress (Yield, Compression Molded) | 11.0 | MPa | ISO 527-2 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Break, 50 µm, Blown Film | 17.0 | MPa | |
| TD : Break, 50 µm, Blown Film | 15.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 50 µm, Blown Film | 300 | % | |
| TD : Break, 50 µm, Blown Film | 540 | % | |
| Dart Drop Impact (50 µm, Blown Film) | 100 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 93.0 | °C | ASTM D1525 |
| Melting Temperature | 111 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 50.0 µm, Blown Film) | > 80 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | < 9.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 to 190 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vydyne® R515J BK0690 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| XENOY™ HX5600HP resin | SABIC Innovative Plastics | PC+PBT | XENOY™ |
| Xuchuan CPU-1195/B-8260 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Caltex PP MU40GB | GS Caltex | PP, Unspecified | Caltex PP |
| DENKA POVAL NP-05F | Denka Company Limited | PVOH | DENKA POVAL |