GELOY™ XP7550 resin
| Category: | ASA+PC , Acrylonitrile Styrene Acrylate + PC |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | GELOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5SiR2x_GELOY-XP7550-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Injection molding ASA-PC Blend suitable for exterior applications featuring outdoor weatherability, toughness, good heat performance and excellent flow. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 14 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 26.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow 1 | 0.50 to 0.70 | % | |
| Flow : 3.20 mm | 0.40 to 0.60 | % | |
| Across Flow : 3.20 mm | 0.50 to 0.70 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.80 | % | |
| Equilibrium, 23°C, 50% RH | 0.30 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 109 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 2550 | MPa | ASTM D638 |
| -- | 2550 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 56.0 | MPa | ASTM D638 |
| Yield | 55.0 | MPa | ISO 527-2/50 |
| Break 4 | 44.0 | MPa | ASTM D638 |
| Break | 44.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 5 | 4.0 | % | ASTM D638 |
| Yield | 3.8 | % | ISO 527-2/50 |
| Break 6 | 40 | % | ASTM D638 |
| Break | 37 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 7 | 2480 | MPa | ASTM D790 |
| -- 8 | 2400 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 74.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 9 | 82.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 10(23°C) | 40 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 53 | J/m | ASTM D256 |
| 23°C | 380 | J/m | ASTM D256 |
| -30°C 11 | 9.0 | kJ/m² | ISO 180/1A |
| 23°C 12 | 35 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C, Total Energy | 10.0 | J | |
| 23°C, Total Energy | 36.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 104 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 13 | 103 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 89.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 14 | 89.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 105 | °C | ASTM D1525, ISO 306/B50 11 15 |
| -- | 106 | °C | ISO 306/B120 |
| CLTE | |||
| Flow : -40 to 40°C | 7.2E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Transverse : -40 to 40°C | 7.9E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 7.8E-5 | cm/cm/°C | ISO 11359-2 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°, Untextured) | 94 | ASTM D523 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 87.8 to 98.9 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Shot Size | 40 to 80 | % | |
| Rear Temperature | 232 to 249 | °C | |
| Middle Temperature | 238 to 254 | °C | |
| Front Temperature | 243 to 260 | °C | |
| Nozzle Temperature | 238 to 254 | °C | |
| Processing (Melt) Temp | 254 to 271 | °C | |
| Mold Temperature | 54.4 to 71.1 | °C | |
| Back Pressure | 0.345 to 1.03 | MPa | |
| Screw Speed | 30 to 80 | rpm | |
| Vent Depth | 0.038 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 5.0 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | Type I, 50 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 sp=62mm |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 mm |
| 14 . | 80*10*4 mm |
| 15 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene MBW2888 | Teknor Apex Asia Pacific PTE. LTD. | PE, Unspecified | Sinpolene |
| Tritan™ MXF121 | Eastman Chemical Company | Copolyester | Tritan™ |
| Vydyne® 75HB NT0679 | Ascend Performance Materials Operations LLC | Nylon 66/6 | Vydyne® |
| APEX® 586 | Teknor Apex Company | PVC, Flexible | APEX® |
| ASI POLYETHYLENE LP 502-01 | A. Schulman Inc. | HDPE, HMW | ASI POLYETHYLENE |