Braskem PE SGF4960
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5SaxYS_Braskem-PE-SGF4960.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SGF4960 is a homopolymer high-density polyethylene, developed for the blow-molding segment with high density and stiffness combined with high impact resistance. The minimum biobased content of this grade is 96%, determined according to ASTM D6866. Application: Bottles for food applications such as dairy products and beverages; Rigid containers for non-food applications such as cosmetics and lubricant oils; Caps & closures molded by compression; Rigid containers for pharmaceutical applications (complies with USP 33). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.962 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.34 | g/10 min | |
| 190°C/21.6 kg | 28 | g/10 min | |
| Environmental Stress-Cracking Resistance 1(50°C, 2.00 mm, 100% Igepal, Compression Molded, F50) | 25.0 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 64 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, Compression Molded | 30.0 | MPa | |
| Break, Compression Molded | 35.0 | MPa | |
| Flexural Modulus - 1% Secant (Compression Molded) | 1400 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 230 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, Compression Molded) | 79.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 129 | °C | ASTM D1525 2 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Biobased Content | > 96 | % | ASTM D6866 |
| Note Message | |
|---|---|
| 1 . | 0.3 mm notched-plaques |
| 2 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| APEX® 3311-60NT | Teknor Apex Company | PVC, Flexible | APEX® |
| Fluorosite 600 - GML | UNIFLON | PTFE | Fluorosite |
| Kynar® 711 | Arkema | PVDF | Kynar® |
| LEXAN™ 3413HF resin | SABIC Innovative Plastics | PC | LEXAN™ |
| OMIKRON HR 50 NAT | TECNOPOL | PP Homopolymer | OMIKRON |