Sinvicomp SSZ4609M
| Category: | PVC, Flexible , Flexible Polyvinyl Chloride |
| Manufacturer: | Teknor Apex Asia Pacific PTE. LTD. |
| Trademark: | Sinvicomp |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5S8Wae_Sinvicomp-SSZ4609M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| "Sinvicomp"SSZ 4609M is a wire & cable polyvinylchloride compound available in pellet form. SSZ 4609M provides good performance for jacketing of cables. |
| General Information | |
|---|---|
| Uses |
|
| Cable Type (IEC 60502) |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 90 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 16.0 | MPa | IEC 60811-1-1 |
| Tensile Elongation (Break) | 250 | % | IEC 60811-1-1 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Changes in mechanical properties after hot air aging test, 100°C, 168 hr 1 | IEC 811-1-2 | ||
| Tensile strength change | 5 | % | IEC 811-1-2 |
| Change in tensile elongation | 15 | % | IEC 811-1-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -18.0 | °C | ASTM D746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (20°C) | 1.0E+13 | ohms·cm | BS 2782 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Loss of Mass - 7 days, 100±2°C 2(100°C) | 1.40 | mg/cm² | IEC 811-3-2 |
| Typical temperature profile for processing SINVICOMP compound is from 160°C to 180°C. The optimum temperatures depend on the type of machine as well as screw design being used to process SINVICOMP.Feeding zone: 160°CCompression zone: 160°C~170°CMixing zone: 170°C~180°CNozzle/Die Zone: 180°C |
| Note Message | |
|---|---|
| 1 . | 100±2°C |
| 2 . | 7 days, 100±2°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® C 216 NATURAL | Solvay Engineering Plastics | Nylon 6 | TECHNYL® C |
| XYRON™ 100V | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| Beetle® PBTC115F | Teknor Apex Company (Chem Polymer) | PBT+PET | Beetle® |
| Infino CF-3300LW | LOTTE ADVANCED MATERIALS CO., LTD. | PC | Infino |
| 3M™ Dyneon™ Fluoroelastomer FC 1640 | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |