TAROLOX 2050 W G4
| Category: | PBT+PET , Polybutylene Terephthalate + PET |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROLOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5R2D5E_TAROLOX-2050-W-G4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT/PET alloy 20% glass fibres reinforced, very good surface appearance, high temperature and chemical resistance. High dimensional stability with low moisture absorption. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.47 - 1.49 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction | 0.60 - 1.0 | % | Internal method |
| Flow direction | 0.40 - 0.80 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ISO 62 |
| Granule Humidity 1 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content 2(750°C) | 20 | % | ISO 3451 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 105 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/50 |
| Flexural Modulus 3 | 6200 | MPa | ISO 178 |
| Flexural Stress 4 | 160 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 40 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 56 | J/m | ASTM D256 |
| 23°C | 70 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, not annealed | 210 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 170 | °C | ISO 75-2/A |
| Continuous Use Temperature 6 | 130 | °C | IEC 60216 |
| Vicat Softening Temperature | 210 | °C | ISO 306/B50 |
| Ball Pressure Test (215°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature | 235 | °C | ISO 11357-3 |
| CLTE - Flow (-30 to 30°C) | 4.2E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric Strength (3.20 mm) | 20 | kV/mm | IEC 60243-1 |
| Dielectric Constant | 3.40 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.970 mm | HB | UL 94 | |
| 1.60 mm | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Oxygen Index | 19 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 130 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 250 - 280 | °C | |
| Mold Temperature | 90.0 - 130 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Pre-heat Temperature: 130 to 150°CPre-heat Time: 2 to 3 hr |
| Note Message | |
|---|---|
| 1 . | TARO 002 |
| 2 . | 1 hr |
| 3 . | 1.0 mm/min |
| 4 . | 1.0 mm/min |
| 5 . | 120°C/hr |
| 6 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYREX® PG-22 | CHI MEI CORPORATION | PS (GPPS) | POLYREX® |
| POWERSIL® 3540 | Wacker Chemie AG | Silicone | POWERSIL® |
| ALTECH® NXT PP-H A 2030/457 HH GF30 CP | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® NXT PP-H |
| Fluoroplex B 60 - GML | UNIFLON | PTFE | Fluoroplex |
| Hapflex™ 790-5 | Hapco Inc. | TP, Unspecified | Hapflex™ |