TARODUR 100 MTR
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TARODUR |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5PZ5fK_TARODUR-100-MTR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ABS with higher thermal resistance. Very good combination of mechanical and thermal properties. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction | 0.50 - 0.70 | % | Internal method |
| Flow direction | 0.50 - 0.70 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.15 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 47.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 35 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2500 | MPa | ISO 178 |
| Flexural Stress 2 | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 18 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 170 | J/m | ASTM D256 |
| Notched Izod Impact (23°C) | 20.0 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed) | 100 | °C | ISO 75-2/A |
| Continuous Use Temperature 4 | 75.0 | °C | IEC 60216 |
| Vicat Softening Temperature | |||
| -- | 112 | °C | ISO 306/A50 |
| -- | 105 | °C | ISO 306/B50 |
| Ball Pressure Test (90°C) | Pass | IEC 60695-10-2 | |
| CLTE - Flow (-30 to 30°C) | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Oxygen Index | < 21 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 1.0 | hr | |
| Processing (Melt) Temp | 210 - 240 | °C | |
| Mold Temperature | 50.0 - 80.0 | °C | |
| Injection Rate | Fast |
| Injection instructions |
|---|
| Pre-heat Temperature: 70 to 80°CPre-heat Time: 3 hrs |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 1.0 mm/min |
| 3 . | 120°C/hr |
| 4 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEO-ZEX™ 2006H | Prime Polymer Co., Ltd. | LLDPE | NEO-ZEX™ |
| Delrin® 127UV NC010 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| HOPELEX PC-1150UR | Lotte Chemical Corporation | PC | HOPELEX |
| Iupilon® CLV1000 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| SIBUR Synthetic Rubber SBS L 30-01A | SIBUR | SBS | SIBUR Synthetic Rubber |