Hifax CA 10 A
| Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hifax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5PRHtI_Hifax-CA-10-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hifax CA 10 A is a reactor TPO (thermoplastic polyolefin) manufactured using the LyondellBasell proprietary Catalloy process technology. It is suitable for industrial applications where a combination of good processability and excellent softness is required. It is widely used as building block resin for flexible water-proofing membranes. Hifax CA 10 A exhibits low stiffness, low hardness and good impact resistance. The grade is available in natural pellet form. For regulatory compliance information see Hifax CA 10 A Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.880 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.60 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 30 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Yield, Compression Molded | 6.00 | MPa | ISO 527-2/500 |
| Break | 11.0 | MPa | ISO 527-2 |
| Break, Compression Molded | 20.0 | MPa | ISO 527-2/500 |
| Tensile Strain | |||
| Break | > 500 | % | ISO 527-2 |
| Break, Compression Molded | 800 | % | ISO 527-2/500 |
| Flexural Modulus | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -20°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 40.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 32.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 60.0 | °C | ISO 306/A50 |
| Melting Temperature | 142 | °C | ISO 11357-3 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MIDILENA III PPJ500 | ROMPETROL PETROCHEMICALS S.R.L. | PP Homopolymer | MIDILENA III |
| VITAMIDE® AS10NT6050 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| YUNGSOX® PP 1600D | Formosa Polypropylene | PP Homopolymer | YUNGSOX® PP |
| Chemfluor PFA | Saint Gobain - Norton | PFA | Chemfluor |
| Karina RED COLOR CONCENTRATE 42/268-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |