Lucent PC PC/PBT-FR5
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Lucent Polymers, Inc. |
| Trademark: | Lucent PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5OoQzg_Lucent-PC-PC-PBT-FR5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Flame Retardant Polycarbonate+PBT Natural and Colors Available Add "R" for Added Release Add "U" for UV Stabilizer UL Listed f1, 5VA at 3.0 mm, V-0 at 1.5 mm |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 25 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.70 | % | |
| Outdoor Suitability | f1 | UL 746C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 53.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 50 | % | ASTM D638 |
| Flexural Modulus | 2120 | MPa | ASTM D790 |
| Flexural Strength | 73.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 3.18 mm | 190 | J/m | |
| 23°C, 3.18 mm | 530 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 98.9 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | 5VA |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TROGAMID® T TX7389 | Evonik Industries AG | Nylon 6/3T | TROGAMID® T |
| XANTAR® 22 UR | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| Ultralloy™ 910 | Hapco Inc. | TP, Unspecified | Ultralloy™ |
| Hyundai EP PA6 LS610 | HYUNDAI EP Co., Ltd. | Nylon 6 | Hyundai EP PA6 |
| Jampilen RP348U | Jam Polypropylene Company | PP Random Copolymer | Jampilen |