OnFlex™ S KA 60A-3S1769
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | OnFlex™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5NrxbF_OnFlex-S-KA-60A-3S1769.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| OnFlex™-S KA thermoplastic elastomer polymer is mixed with hydrogenated styrene block copolymer. This series of polymers has good compatibility and can provide excellent adhesion to polyamide polymer materials, such as PA6, PA6.6, PA11 and PA12. OnFlex-S KA polymer can be processed by 2K molding or multiple injection molding, plug-in molding or co-extrusion. In addition, OnFlex™-S KA polymer has good compression set even at high temperatures, its processability is good, the hardness range is large, the bending at low temperatures, scratch resistance, coloring, surface appearance, mechanical properties, etc. are good, and excellent UV resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.09 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 60 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 37 | ||
| 100% strain | 2.40 | MPa | ISO 37 |
| 300% strain | 4.20 | MPa | ISO 37 |
| Tensile Stress (Break) | 4.50 | MPa | ISO 37 |
| Tensile Elongation (Break) | 450 | % | ISO 37 |
| Tear Strength | 30 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 13 | % | ISO 815 |
| 70°C, 22 hr | 31 | % | ISO 815 |
| 100°C, 22 hr | 55 | % | ISO 815 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| General Material Type | Styrene thermoplastic elastomers (TES) | ||
| 各项属性值是采用注射模制基板测量得出。 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 200 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Microthene® F FA70900 | LyondellBasell Industries | HDPE | Microthene® F |
| Adell PP EZ-18 | Adell Plastics, Inc. | PP Homopolymer | Adell PP |
| Bashplast Compound SSP-A17 (BP)/CB-B25 (BP) | Bashplast Ltd. | PE, Unspecified | Bashplast Compound |
| Karina WHITE PVC COMPOUND 802-10/55-AY-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POLYelast TPE EDS80 D35 | Polykemi AB | PP+EPDM | POLYelast |