LEXAN™ LUX9610 resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5NdiZK_LEXANLUX9610resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LEXAN LUX9610 is a UV stabilized flame retardant transparent polycarbonate featuring non brominated and non chlorinated FR system with good flow and thin wall FR performance providing good colorstability under heat exposure. Developed for lightguide and LED applicatons. It meets WEEE/RoHS requirements for various applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 7.0 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 7.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.60 - 0.80 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.35 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.15 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2300 | MPa | ASTM D638 |
| -- | 2230 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 62.0 | MPa | ASTM D638 |
| Yield | 62.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 65.0 | MPa | ASTM D638 |
| Fracture | 58.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 6.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50 |
| Fracture 5 | 85 | % | ASTM D638 |
| Fracture | 77 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2160 | MPa | ASTM D790 |
| -- 7 | 2250 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 95.0 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 95.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 760 | J/m | ASTM D256 |
| -30°C 9 | 18 | kJ/m² | ISO 180/1A |
| 23°C 10 | 70 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 70.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, unannealed, 64.0mm span 11 | 136 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 125 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 12 | 125 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 142 | °C | ASTM D1525 13 |
| -- | 145 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 6.8E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 6.7E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | 125 | °C | UL 746 |
| RTI Imp | 115 | °C | UL 746 |
| RTI | 125 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 1 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 850 | °C | IEC 60695-2-13 |
| 1.50 mm | 850 | °C | IEC 60695-2-13 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.586 | ISO 489 | |
| Transmittance | |||
| 2540 µm | > 90.0 | % | ASTM D1003 |
| 2540 µm, 420 nm | > 88.0 | % | Internal method |
| Haze (2000 µm) | 1.0 | % | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 260 - 280 | °C | |
| Middle Temperature | 270 - 290 | °C | |
| Front Temperature | 280 - 310 | °C | |
| Nozzle Temperature | 270 - 290 | °C | |
| Processing (Melt) Temp | 280 - 310 | °C | |
| Mold Temperature | 80.0 - 110 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*3 |
| 10 . | 80*10*3 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| 13 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mar-Bal MB2000-15 | Mar-Bal, Inc. | Polyester, TP | Mar-Bal |
| Akulon® XP36-E1 | DSM Engineering Plastics | Nylon 6 | Akulon® |
| Comai 109-1 NT | Comai Ltda | PP Homopolymer | Comai |
| Fainplast PVC CKL 64/K | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Echo® RPPC 20/10 BK | Ravago Manufacturing Americas, LLC | PP Copolymer | Echo® |