SUMIKASUPER LCP is a thermotropic liquid crystalline polyester, showing the highest heat resistance among engineering plastics. SUMIKASUPER LCP E6810F is a sliding grade that contains glass fiber reinforcement, an inorganic filler and fluororesin. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.79 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.22 | % | ASTM D955 |
| Transverse flow | 0.87 | % | ASTM D955 |
| Water Absorption (Saturation) | 0.020 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 109 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.5 | % | ASTM D638 |
| Flexural Modulus | 11100 | MPa | ASTM D790 |
| Flexural Strength | 114 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact | 340 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 280 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.380 mm) | V-0 | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, Sumitomo Chemical Method, Machine Direction: 2.2 mils/inMold Shrinkage, Sumitomo Chemical Method, Transverse Direction: 8.7 mils/in |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Regrind | 30 | % | |
| Rear Temperature | 300 - 320 | °C | |
| Middle Temperature | 320 - 350 | °C | |
| Front Temperature | 340 - 370 | °C | |
| Nozzle Temperature | 340 - 370 | °C | |
| Mold Temperature | 70.0 - 160 | °C | |
| Injection Pressure | 78.0 - 157 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 20.0 - 39.0 | MPa | |
| Back Pressure | 0.980 - 4.90 | MPa | |
| Screw Speed | 50 - 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SRG7565 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Vi-Chem PVC VNC90-60I | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Wanthane® WHT-1570 | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | Wanthane® |
| ANYPOL SE-160LL | SH Energy & Chemical | PS (EPS) | ANYPOL |
| Elastron® G G501.A23.N | Elastron USA, Inc. | SEBS | Elastron® G |