CYCOLOY™ CM4300 resin
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | CYCOLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5NGlPz_CYCOLOY-CM4300-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CYCOLOY EXCY0372 is a 20% glass reinforced PC+ABS blend for injection molding purposes, featuring of balanced properties of high modulus, good flow and ductility. It is of Br- & Cl-free flame retardant systems. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 12.0 | cm³/10min | ISO 1133 |
| Water Absorption (Saturation, 23°C) | 0.15 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 7000 | MPa | ASTM D638 |
| Tensile Stress (Break) | 100 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 6700 | MPa | ISO 178 |
| Flexural Stress | 150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 80 | J/m | ASTM D256 |
| -30°C 3 | 9.0 | kJ/m² | ISO 180/1A |
| 23°C 4 | 9.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 5(23°C) | 31 | kJ/m² | ISO 180/1U |
| Multi-Axial Instrumented Impact Energy | 11.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 90.0 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 94.0 | °C | |
| Vicat Softening Temperature | |||
| -- | 93.0 | °C | ASTM D1525 6 |
| -- | 98.0 | °C | ISO 306/B120 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 2.0E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 5.0E-5 | cm/cm/°C | |
| Thermal Conductivity (50°C) | 0.20 | W/m/K | ASTM C177 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-1 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Rear Temperature | 230 to 270 | °C | |
| Middle Temperature | 240 to 280 | °C | |
| Front Temperature | 250 to 280 | °C | |
| Nozzle Temperature | 250 to 280 | °C | |
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Back Pressure | 3.00 to 9.00 | MPa | |
| Screw Speed | 30 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*3 |
| 4 . | 80*10*3 |
| 5 . | 80*10*3 |
| 6 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren M2500CD (On-spec.) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| Moplen EP340K | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| APICAL 300AV | Kaneka Corporation | PI, TS | APICAL |
| Lionpol LC-60063 | Lion Polymers Incorporated | TPE | Lionpol |
| LNP™ LUBRICOMP™ UFL36AS compound | SABIC Innovative Plastics | PPA | LNP™ LUBRICOMP™ |