VYTEEN PC/ABS 3016
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Lavergne Group |
| Trademark: | VYTEEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5N856Y_VYTEEN-PC-ABS-3016.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Vyteen PC/ABS 3016 is a black 16% glass fiber reinforced Polycarbonate/ABS alloy designed for injection molding Features
Typical Applications
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.22 | g/cm³ | ASTM D792 |
| 23°C | 1.20 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 2.00mm | 4.9 - 6.5 | % | ASTM D955 |
| 3.20 mm | 0.30 - 0.50 | % | ISO 294-4 |
| Ash Content | |||
| -- | 16 | % | ISO 3451 |
| -- | 16 | % | ASTM D2854 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 80.0 | MPa | ASTM D638 |
| Fracture | 75.0 | MPa | ISO 527-2/5 |
| Flexural Modulus | |||
| -- 2 | 5300 | MPa | ASTM D790 |
| -- 3 | 5250 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 140 | MPa | ASTM D790 |
| -- 5 | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/A | ||
| -30°C | 6.0 | kJ/m² | ISO 179/A |
| 23°C | 8.0 | kJ/m² | ISO 179/A |
| Notched Izod Impact | ASTM D256 | ||
| -29°C | 85 | J/m | ASTM D256 |
| 23°C | 93 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 112 | °C | ASTM D648, ISO 75-2/A |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 100 | mm/min | SAE J369 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 200 - 230 | °C | |
| Middle Temperature | 240 - 250 | °C | |
| Front Temperature | 260 - 275 | °C | |
| Nozzle Temperature | 270 - 280 | °C | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Injection Pressure: MediumBack Pressure: LowScrew Speed: Low |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAMID™ TA210SG30 | Mando Advanced Materials Co., Ltd. | Nylon 66 | TEKAMID™ |
| XYRON™ DG141 | Asahi Kasei Chemicals Corporation | PPS+PPE | XYRON™ |
| Grivory® XE 4102 black 9238 | EMS-GRIVORY | Nylon 10T/X | Grivory® |
| KPOL-HDPE HD K-I 14/960 | KPOL Chem Co. | HDPE | KPOL-HDPE |
| LNP™ LUBRICOMP™ RX01514 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |