ATTANE™ 4203
| Category: | ULDPE , Ultra Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ATTANE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5MRo6Y_ATTANE-4203.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Puncture Energy | 4.52 | J | Internal method |
| Film Puncture Force | 48.9 | N | Internal method |
| Film Puncture Resistance | 24.8 | J/cm³ | Internal method |
| Film strength | ASTM D882 | ||
| MD | 45.5 | J/cm³ | ASTM D882 |
| TD | 64.5 | J/cm³ | ASTM D882 |
| secant modulus | ASTM D882 | ||
| 1% secant, MD | 98.6 | MPa | ASTM D882 |
| 2% secant, MD | 89.6 | MPa | ASTM D882 |
| 1% secant, TD | 113 | MPa | ASTM D882 |
| 2% secant, TD | 93.8 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 6.21 | MPa | ASTM D882 |
| TD : Yield | 5.86 | MPa | ASTM D882 |
| MD : Fracture | 32.4 | MPa | ASTM D882 |
| TD : Fracture | 30.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 340 | % | ASTM D882 |
| TD : Fracture | 570 | % | ASTM D882 |
| Dart Drop Impact | > 1100 | g | ASTM D1709B |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 370 | g | ASTM D1922 |
| TD | 520 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 83.9 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 123 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 39 | ASTM D2457 | |
| Haze | 14 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：3.5 英寸 螺杆类型：DSB II 模具间隙：70 密尔 (1.8 mm) 熔体温度：419°F 输出：模具周长的 12 磅/小时/英寸 模具直径：8 英寸 放大比：2.5:1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NOVAREX® M7027BF | Mitsubishi Engineering-Plastics Corp | PC | NOVAREX® |
| CELLIFF® 7000 | Microcell Composite Company | SBS | CELLIFF® |
| Gebalon PC ULtimate G10 FR(y) | geba Kunststoffcompounds GmbH | PC | Gebalon |
| Hostacom M4 N01 L255013 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| Kumho SBR 1793 | Korea Kumho Petrochemical Co., Ltd. | SBR, Emulsion | Kumho SBR |