Baytec® SPR-092A
| Category: | PUR-Ether/MDI , Polyurethane (Polyether, MDI) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Baytec® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5MOYtU_Baytec-SPR-092A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Baytec SPR-092A is a two-component, 100%-solids spray system with a Shore A hardness of 92. The isocyanate component is a modified diphenylmethane diisocyanate (MDI) prepolymer, and the polyol component is a polyether polyol blend. The system has added UV stabilizers and is used in spray applications to improve the corrosion, weather, and abrasion resistance of various surfaces. In-mold application is also possible. Typical applications include protective layers for pipes, tanks, fabrics, wood, flexible foams, and other industrial surfaces. The system can be pigmented to almost any color. As with any product, use of the Baytec SPR-092A system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Additive |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Water absorption rate- 30 days | 1.5 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 92 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Taber Abrasion Resistance (1000 Cycles, 1000 g, H-18 Wheel) | 150 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 15.2 - 15.9 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 490 - 580 | % | ASTM D412 |
| Tear Strength | |||
| -- 1 | 59.5 - 71.8 | kN/m | ASTM D624 |
| Cracking | 19 - 23 | kN/m | ASTM D1938 |
| Thermoset | Nominal Value | ||
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mixing ratio by weight: 100 | ||
| Component B | Mixing ratio by weight: 100 |
| Additional Information |
|---|
| Part A Type: Isocyanate Appearance: Yellowish liquid Specific Gravity @ 25°C: 1.09 Viscosity @25°C: 2500 mPa Flash Point, PMCC: 216°C NCO: 9.8 wt% Part B Type: Polyol Appearance: White liquid Specific Gravity @ 25°C: 1.04 Viscosity @25°C: 1500 mPa-s Flash Point, PMCC: 179°C Hydroxyl Number: 130 mg KOH/g Material Temperature: 25 to 60°CGel Time: 12 to 15 secTack-Free: 1 minHandling: 30 min |
| Note Message | |
|---|---|
| 1 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Starflam PF0023E | Eurostar Engineering Plastics | Nylon 6 | Starflam |
| Crastin® SK642FR BK851 | DuPont Performance Polymers | PBT | Crastin® |
| DIC.PPS FZ-2140 | DIC Corporation | PPS | DIC.PPS |
| Karina BEIGE PVC COMPOUND 650D08/224-D-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ EX93452 compound | SABIC Innovative Plastics | PEI | LNP™ THERMOCOMP™ |