Starex AS-0151BS
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5M3Ww6_Starex-AS-0151BS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Anti-static material that can be applied to the housing of OA devices, videotape case, IC, LSI carrier etc. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.05 | g/cm³ | ASTM D792 |
| -- | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 3.5 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 109 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 1 | 40.0 | MPa | ASTM D638 |
| Yield | 41.0 | MPa | ISO 527-2/50 |
| Break | 34.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 19 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 2 | 2200 | MPa | ASTM D790 |
| -- 3 | 2200 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 59.0 | MPa | ASTM D790 |
| -- 5 | 63.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 6(23°C) | 21 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 6.35 mm | 210 | J/m | ASTM D256 |
| 23°C 7 | 20 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 4.00 mm | 88.0 | °C | ISO 75-2/B |
| 0.45 MPa, Annealed | 97.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 4.00 mm | 76.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed, 4.00 mm | 93.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 96.0 | °C | ISO 306/B50 |
| -- | 97.0 | °C | ISO 306/B120 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 | °C | |
| Desiccant Dryer | 80.0 | °C | |
| Drying Time | |||
| -- | 2.0 to 4.0 | hr | |
| Desiccant Dryer | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 160 to 180 | °C | |
| Middle Temperature | 190 to 200 | °C | |
| Front Temperature | 210 to 220 | °C | |
| Nozzle Temperature | 230 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 49.0 to 147 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 2.8 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | Thickness: 4 mm |
| 7 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® Fine Powders T GREY 5161 MAC | Arkema | Nylon 11 | Rilsan® Fine Powders |
| Manner Flexible PVC M8175 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Matrixx CPP1C45HSBK | The Matrixx Group, Inc. | PP Copolymer | Matrixx |
| ROTOLENE S® 95065 | Polimeros Mexicanos s.a. de c.v. | HDPE | ROTOLENE S® |
| Hybrid S493 | Ravago Manufacturing Americas, LLC | PC Alloy | Hybrid |