Retelan® S NERO
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Retelan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5Lq5cK_Retelan-S-NERO.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ABS grade with high impact resistance, easy flowing, excellent gloss |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage | 0.50 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 44.0 | MPa | |
| Break | 36.0 | MPa | |
| Tensile Elongation (Break) | 20 | % | ASTM D638 |
| Flexural Modulus | 2500 | MPa | ASTM D790 |
| Flexural Strength | 70.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 200 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 100 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 105 | °C | ASTM D1525 1 |
| -- | 98.0 | °C | ASTM D1525 2 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Volume Resistivity (23°C) | 1.0E+13 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.60 mm) | 30 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 3.10 | ASTM D150 | |
| Dissipation Factor (1 kHz) | 4.0E-3 | ASTM D150 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 190 | °C | |
| Middle Temperature | 210 | °C | |
| Front Temperature | 230 | °C | |
| Mold Temperature | 50.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 1 (10 N) |
| 2 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PolyFR™ 200 | JJI Technologies, LLC | PP, Unspecified | PolyFR™ |
| tefanyl® VE VEEP 100 | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | tefanyl® VE |
| THERMORUN® Z101N | Mitsubishi Chemical Performance Polymers, Inc. | TPE | THERMORUN® |
| Kazan LDPE 102-03K | Kazanorgsintez Joint Stock Company | LDPE | Kazan LDPE |
| Lucon® PS6090 | LG Chem Ltd. | ABS | Lucon® |