Generic ABS+PC - Glass Fiber
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5L4ggS_Generic-ABS-PC---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic ABS+PC - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.17 - 1.43 | g/cm³ | ASTM D792 |
| 23°C | 1.17 - 1.43 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 250°C/2.16 kg | 2.3 - 4.1 | g/10 min | ASTM D1238 |
| 260°C/5.0 kg | 9.7 - 30 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 14.8 - 20.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.15 - 0.43 | % | ASTM D955 |
| Transverse flow : 23°C | 0.25 - 0.65 | % | ASTM D955 |
| 23°C | 0.20 - 0.46 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.098 - 0.10 | % | ASTM D570 |
| 23°C, 24 hr | 0.29 - 0.60 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 - 0.25 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 111 - 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 3450 - 9650 | MPa | ASTM D638 |
| 23°C | 3300 - 7800 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 58.3 - 125 | MPa | ASTM D638 |
| Yield, 23°C | 58.3 - 95.6 | MPa | ISO 527-2 |
| Fracture, 23°C | 48.8 - 110 | MPa | ASTM D638 |
| Fracture, 23°C | 50.9 - 95.1 | MPa | ISO 527-2 |
| 23°C | 73.1 - 125 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 2.5 - 5.0 | % | ASTM D638 |
| Yield, 23°C | 2.1 - 5.5 | % | ISO 527-2 |
| Fracture, 23°C | 1.5 - 7.4 | % | ASTM D638 |
| Fracture, 23°C | 2.0 - 5.1 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 2450 - 8580 | MPa | ASTM D790 |
| 23°C | 3000 - 8230 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 94.3 - 173 | MPa | ASTM D790 |
| 23°C | 92.3 - 144 | MPa | ISO 178 |
| Yield, 23°C | 101 - 138 | MPa | ASTM D790 |
| Fracture, 23°C | 99.7 - 142 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.9 - 10 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 25 - 40 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 58 - 130 | J/m | ASTM D256 |
| 23°C | 4.0 - 14 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 310 - 800 | J/m | ASTM D256 |
| 23°C | 21 - 38 | kJ/m² | ISO 180 |
| Instrumented Dart Impact (23°C) | 13.3 - 35.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 92.0 - 139 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 89.0 - 140 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 87.5 - 136 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 112 - 124 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 101 - 144 | °C | ASTM D1525 |
| -- | 99.4 - 140 | °C | ISO 306 |
| Linear thermal expansion coefficient | |||
| Flow | 2.9E-5 - 6.1E-5 | cm/cm/°C | ASTM D696 |
| Flow | 2.9E-5 - 7.7E-5 | cm/cm/°C | ASTM E831 |
| Flow | 1.7E-5 - 7.7E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 6.5E-5 - 8.2E-5 | cm/cm/°C | ASTM D696 |
| Lateral | 3.2E-5 - 7.3E-5 | cm/cm/°C | ASTM E831 |
| Lateral | 7.9E-5 - 8.3E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 1.0E+2 - 2.5E+14 | ohms | ASTM D257 |
| -- | 9.8E+14 - 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 5.1E+5 - 1.3E+16 | ohms·cm | ASTM D257 |
| 23°C | 1.0E+13 - 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C) | 26 - 36 | kV/mm | ASTM D149 |
| Arc Resistance | 69.0 - 106 | sec | ASTM D495 |
| Comparative Tracking Index | 100 - 256 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | 15.0 - 150 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | 64.0 - 300 | mm/min | UL 746 |
| Hot-wire Ignition (HWI) | 26 - 150 | sec | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Ignition Temperature | 642 - 755 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 106 | °C | |
| Drying Time | 3.4 - 5.0 | hr | |
| Dew Point | -28.9 - -28.6 | °C | |
| Suggested Max Moisture | 0.019 - 0.020 | % | |
| Suggested Shot Size | 50 - 60 | % | |
| Rear Temperature | 214 - 270 | °C | |
| Middle Temperature | 234 - 280 | °C | |
| Front Temperature | 245 - 285 | °C | |
| Nozzle Temperature | 235 - 286 | °C | |
| Processing (Melt) Temp | 249 - 291 | °C | |
| Mold Temperature | 59.4 - 81.4 | °C | |
| Injection Pressure | 85.9 - 87.9 | MPa | |
| Back Pressure | 0.0392 - 12.5 | MPa | |
| Screw Speed | 45 - 75 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic ABS+PC - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4085U | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| SUPRAN® LFT PA A1350 | SAMBARK | Nylon 66 | SUPRAN® LFT PA |
| FHR Polypropylene P4C5B-181B | Flint Hills Resources, LP | PP Homopolymer | FHR Polypropylene |
| INSULCAST® 140 FR/INSULCURE 11B | ITW Polymers Coatings North America | Epoxy | INSULCAST® |
| ULTEM™ EXUM0169 resin | SABIC Innovative Plastics | PEI | ULTEM™ |