AvaSpire® AV-651 GF50

Category:	PAEK , Polyaryletherketone
Manufacturer:	Solvay Specialty Polymers
Trademark:	AvaSpire®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	5KkZTr_AvaSpireAV651GF50.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

AvaSpire® AV-651 GF50 is a 50% chopped glass fiber-reinforced polyaryletherketone (PAEK) resin. It has been specifically formulated to provide exceptionally high strength and stiffness at elevated temperatures along with very strong chemical resistance to a broad range of harsh chemical environments encountered across a wide variety of industries and engineering applications. Typical potential applications for AV-651 GF50 include orthopedic and dental instruments, under-the-hood automotive parts, and parts in the chemical and oil and gas industries. This grade is easily injection moldable into precision molded parts.

Typical property data provided are based on a limited production history.

Beige: AvaSpire® AV-651 GF50 BG 20

Black: AvaSpire® AV-651 GF50 BK 95

General Information
Filler / Reinforcement	Glass fiber reinforced material, 50% filler by weight
Features	Good dimensional stability Electron beam disinfection Radioactive permeable Radiation disinfection Rigidity, high High strength Pressure cooker disinfection Good disinfection Ethylene oxide disinfection Anti-gamma radiation Good chemical resistance Fatigue resistance Heat resistance, high Steam resistance thermal disinfection Biocompatibility Disinfect with steam Flame retardancy
Uses	Electrical/Electronic Applications Aircraft applications Industrial application Connector Seals Application in Automobile Field Surgical instruments Dental application field Medical/nursing supplies Medical equipment Medical devices
RoHS Compliance	Contact manufacturer
Appearance	Black Beige
Forms	Particle
Processing Method	Machining Profile extrusion molding Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.73	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (400°C/2.16 kg)	5.0	g/10 min	ASTM D1238
Water Absorption (24 hr)	0.10	%	ASTM D570

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus ¹	17900	MPa	ASTM D638
Tensile Strength ²	199	MPa	ASTM D638
Tensile Elongation ³(Break)	2.1	%	ASTM D638
Flexural Modulus	16500	MPa	ASTM D790
Flexural Strength	297	MPa	ASTM D790
Flexural Elongation at Break	2.2	%	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	110	J/m	ASTM D256
Unnotched Izod Impact	960	J/m	ASTM D4812

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Annealed, 3.20 mm)	287	°C	ASTM D648
Glass Transition Temperature	158	°C	ASTM D3418
Peak Melting Temperature	340	°C	ASTM D3417

Fill Analysis	Nominal Value	Unit	Test Method
Melt Viscosity (400°C, 1000 sec^-1)	630	Pa·s	ASTM D3835

Injection	Nominal Value	Unit
Drying Temperature	149	°C
Drying Time	4.0	hr
Rear Temperature	365	°C
Middle Temperature	371	°C
Front Temperature	377	°C
Nozzle Temperature	382	°C
Processing (Melt) Temp	366 - 388	°C
Mold Temperature	160 - 190	°C
Injection Rate	Fast
Screw Compression Ratio	2.0 : 1.0 - 3.0 : 1.0

Note Message
1 .	5.0 mm/min
2 .	5.0 mm/min
3 .	5.0 mm/min

Resin Grade	Manufacturer	Category	Trademark
Sanren M700R (On-spec.)	SINOPEC Shanghai Petrochemical Co. Ltd.	PP Copolymer	Sanren
TOLEN H032 TF	SIBUR, LLC	PP Homopolymer	TOLEN
NuSil MED-4810	NuSil Technology	Silicone Rubber, LSR	NuSil
HiFill® PEEK GF15	Techmer Engineered Solutions	PEEK	HiFill®
Ultramid® A3HG6 HR	BASF Corporation	Nylon 66	Ultramid®