Iupilon® GSH2020R2
| Category: | PC , Polycarbonate |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Iupilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5KTIcA_Iupilon-GSH2020R2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Iupilon® GSH2020R2 is a Polycarbonate (PC) material filled with 20% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Iupilon® GSH2020R2: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.35 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 8.5 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 8.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Across Flow : 3.20 mm | 0.30 to 0.50 | % | |
| Flow : 3.20 mm | 0.10 to 0.30 | % | |
| Water Absorption (Saturation, 23°C) | 0.11 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6200 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 104 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.2 | % | ISO 527-2 |
| Flexural Modulus | 5800 | MPa | ISO 178 |
| Flexural Stress | 160 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 13 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 55 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 146 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 143 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | ||
| Flow | 2.6E-5 | cm/cm/°C | |
| Transverse | 6.3E-5 | cm/cm/°C |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.400 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 270 to 290 | °C | |
| Middle Temperature | 280 to 300 | °C | |
| Front Temperature | 290 to 310 | °C | |
| Nozzle Temperature | 290 to 310 | °C | |
| Mold Temperature | 80.0 to 120 | °C | |
| Injection Pressure | 50.0 to 150 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE 2200H2 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| TECHNO ALPHALOY MPC6801 | Techno Polymer Co, Ltd. | PC+ABS | TECHNO ALPHALOY |
| Hifax DG 232 2693 | LyondellBasell Industries | Polyolefin, Unspecified | Hifax |
| ESENTTIA 25H35-SB | Polipropileno del Caribe S.A. | PP Homopolymer | ESENTTIA |
| OnForce™ LFT NN-30 LGF/000 Natural | PolyOne Corporation | Nylon 66 | OnForce™ LFT |