Moplen RP316M
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Moplen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5KOByP_Moplen-RP316M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
"Moplen" RP316M is a slightly modified propylene random copolymer for manufacturing high transparent cast films. The product contains slip, antiblock and antielectrostatic agents. It offers excellent processability, high clarity and gloss and good heat weldability. Main applications are packaging of foodstuffs, packaging of books and stationary. "Moplen" RP316M is suitable for food contact. For regulatory information please refer to "Moplen" RP316M Product Stewardship Bulletin ( PSB ). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 67 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1100 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 28.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 11 | % | |
| Break | 520 | % | |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.20 | ||
| vs. Itself - Static | 0.20 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus - MD 1(50 µm) | 780 | MPa | ASTM D882 |
| Tensile Strength - MD 2 | ASTM D882 | ||
| Yield, 50 µm | 20.0 | MPa | |
| Break, 50 µm | 40.0 | MPa | |
| Tensile Elongation - MD 3 | ASTM D882 | ||
| Yield, 50 µm | 6.3 | % | |
| Break, 50 µm | 730 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| 0°C | 1.4 | kJ/m² | |
| 23°C | 3.4 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 72.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 135 | °C | ISO 306/A50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm) | 88 | ASTM D2457 | |
| Haze (50.0 µm) | < 1.5 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 25 mm/min |
| 2 . | 500 mm/min |
| 3 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Viprene™ P40D-22U-BLK | Alliance Polymers & Services | TPV | Viprene™ |
| Fiberfil® J-60/10/E8 | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| Generic PP, Unspecified - Carbon Fiber | Generic | PP, Unspecified | Generic |
| MARPOL® COPP 35-R-BL | Marco Polo International, Inc. | PP Copolymer | MARPOL® COPP |
| CYCOLAC™ EX39 resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |