NOVALAC RX®475 Datasheet,Phenolic,Vyncolit N.V.-SHANGHAI SUSHENG

Message
NOVALAC RX®475 is a phenolic (Phenolic) material, and its filler is fiber filler. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is: resin transfer molding or compression molding. NOVALAC RX®The main features of the 475 are: chemical resistance Creep resistance Good dimensional stability Typical application areas include: Electrical/electronic applications engineering/industrial accessories electrical appliances House Tools

General Information
Filler / Reinforcement	Fiber filler
Features	Good dimensional stability Low smoke Solvent resistance Good creep resistance alkali resistance acid resistance
Uses	Membrane key switch Pump parts Gear Electrical/Electronic Applications Electrical appliances Power/other tools Connector Application in Automobile Field Shell
Forms	Particle
Processing Method	Resin transfer molding Compression molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.39	g/cm³	ASTM D792
Bulk Factor	3.5		ASTM D1895
Molding Shrinkage - Flow (Compression Molded)	0.20	%	ASTM D955
Water Absorption (23°C, 24 hr)	0.50	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (E-Scale)	65		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength	51.7	MPa	ASTM D638
Flexural Modulus	7580	MPa	ASTM D790
Flexural Strength	65.5	MPa	ASTM D790
Compressive Strength	179	MPa	ASTM D695

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	100	J/m	ASTM D256A

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)	179	°C	ASTM D648
Linear thermal expansion coefficient			ASTM D696
Flow	3.0E-5	cm/cm/°C	ASTM D696
Lateral	5.8E-5	cm/cm/°C	ASTM D696
Thermal Conductivity	0.49	W/m/K	ASTM C177

Electrical	Nominal Value	Unit	Test Method
Dielectric Strength			ASTM D149
-- ¹	0.98	kV/mm	ASTM D149
-- ²	0.98	kV/mm	ASTM D149
Arc Resistance	15.0	sec	ASTM D495

Additional Information
The value listed as Thermal Conductivity, ASTM C177, was tested in accordance with ASTM F433.Water Absorption, ASTM D570, 48 hrs, 50°C: 3.5%Flexural Strain, ASTM D790: 0.89%Dielectric Strength, ASTM D149, 60 Hz, Method A, wet: 25 V/milDielectric Strength, ASTM D149, 60 Hz, Method B, wet: 25 V/milCompression and Transfer Molding Conditions: Preforming Pressure: 8000 to 12000 psi Preheat Temperature: 210 to 235 °F Preheat Time: 45 sec Mold Temperature: 330 to 360 °F Compression Mold Pressure: 2500 to 5000 psi Transfer Mold Pressure: 4000 to 6000 psi Cure Time, 0.125 in: 40 to 50 sec

Additional Information

The value listed as Thermal Conductivity, ASTM C177, was tested in accordance with ASTM F433.Water Absorption, ASTM D570, 48 hrs, 50°C: 3.5%Flexural Strain, ASTM D790: 0.89%Dielectric Strength, ASTM D149, 60 Hz, Method A, wet: 25 V/milDielectric Strength, ASTM D149, 60 Hz, Method B, wet: 25 V/milCompression and Transfer Molding Conditions: Preforming Pressure: 8000 to 12000 psi Preheat Temperature: 210 to 235 °F Preheat Time: 45 sec Mold Temperature: 330 to 360 °F Compression Mold Pressure: 2500 to 5000 psi Transfer Mold Pressure: 4000 to 6000 psi Cure Time, 0.125 in: 40 to 50 sec

Note Message
1 .	Method A (short time)
2 .	Method B (step by step)

Category:	Phenolic , Phenolic
Manufacturer:	Vyncolit N.V.
Trademark:	NOVALAC
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	5Hx4Rb_NOVALAC-RX-475.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
SilTRUST® TSE3664K	Momentive Performance Materials Inc.	Silicone	SilTRUST®
Sylvin 913-80 Natural	Sylvin Technologies Incorporated	PVC, Flexible	Sylvin
APEX® 3201R-75NT	Teknor Apex Company	PVC, Flexible	APEX®
LG PVC LS100E	LG Chem Ltd.	PVC Homopolymer	LG PVC
Zytel® MT409AHS NC010	DuPont Performance Polymers	Nylon 66	Zytel®