Sumikon® PM-9820
| Category: | Phenolic , Phenolic |
| Manufacturer: | SBHPP |
| Trademark: | Sumikon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5HPmLa_SumikonPM9820.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SUMIKON® PM-9820 (Type JR Black) is Organic fiber and Inorganic filler filled resol resin (non-anmonia phenolic) molding compound with good electronic property and heat resistance. This grade is official registered UL with V-0 (t=0.16). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | JIS K6911 |
| Molding Shrinkage - Flow | 0.76 | % | JIS K6911 |
| Water Absorption (Equilibrium) | 0.28 | % | JIS K6911 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 75.0 | MPa | JIS K6911 |
| Flexural Modulus | 7000 | MPa | JIS K6911 |
| Flexural Strength | 110 | MPa | JIS K6911 |
| Compressive Strength | 231 | MPa | JIS K6911 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.5 | kJ/m² | JIS K6911 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 215 | °C | JIS K6911 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 1 | 10 | kV/mm | JIS K6911 |
| Arc Resistance | 130 | sec | JIS K6911 |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Insulation Resistance | JIS K6911 | ||
| -- 2 | 1.0E+11 | ohms | JIS K6911 |
| -- 3 | 1.0E+10 | ohms | JIS K6911 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.160 mm) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | Method B (step by step) |
| 2 . | As molded |
| 3 . | After boiling |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mediprene® 500200M | ELASTO | SEBS | Mediprene® |
| Vipel® F282-AAC-19 | AOC, L.L.C. | Polyester Alloy | Vipel® |
| Abstron HI40I | Bhansali Engineering Polymers Limited | ABS | Abstron |
| Hifax TRC 432P G14008 | LyondellBasell Industries | PP Copolymer | Hifax |
| LNP™ STAT-KON™ ME003S compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ STAT-KON™ |