Latiohm 83-07 PD11 CNT
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latiohm |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5HPgQm_Latiohm8307PD11CNT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Semiconductive/dissipative product based on Polyamide 12 (PA12), impact modified. Carbon nanotubes. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.10 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Transverse flow : 2.00mm | 0.80 - 1.2 | % | ISO 294-4 |
| Flow : 2.00mm | 0.80 - 1.2 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1100 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 35.0 | MPa | ISO 527-2/5 |
| Fracture, 23°C | 35.0 | MPa | ISO 527-2/5 |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 20 | % | ISO 527-2/5 |
| Fracture, 23°C | 85 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 75 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 100 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 40.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 120 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+7 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+8 | ohms·cm | ASTM D257 |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime 8600 | Prime PVC® | PVC, Rigid | Prime |
| YUNGSOX® PP 1124 | Formosa Polypropylene | PP Homopolymer | YUNGSOX® PP |
| ESTADIENE 2525 AS | Cossa Polimeri S.r.l. | ABS | ESTADIENE |
| LG PVC PA1302 | LG Chem Ltd. | PVC Copolymer | LG PVC |
| LNP™ STAT-KON™ DD0009 compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |