TAISOX 7240M
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Formosa Plastics Corporation |
| Trademark: | TAISOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5HBGGR_TAISOX-7240M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TAISOX 7240M is an Ethylene Vinyl Acetate Copolymer (EVA) material. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of TAISOX 7240M are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.935 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.5 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 15.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 42 92 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 5.39 | MPa | |
| Break | 14.7 | MPa | |
| Tensile Elongation (Break) | 700 | % | ASTM D638 |
| Flexural Modulus | 20.6 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 65.0 | °C | ASTM D1525 |
| Melting Temperature | 87.0 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 150 to 180 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD A 100 | RTP Company | PP, Unspecified | RTP |
| Viprene™ P85A-22U-NAT | Alliance Polymers & Services | TPV | Viprene™ |
| Bionate® 90A | DSM Biomedical Inc. | PC+TPU | Bionate® |
| EMOPLEN® HP MTF 5 | EMAS Plastik San.Tic.AS. | PP Homopolymer | EMOPLEN® |
| IROGRAN® A 94 E 4900 | Huntsman Corporation | TPU-Polyester | IROGRAN® |