Innothane® IE-52A
| Category: | TSU-Ether , Polyurethane Thermoset Elastomer, Polyether Based |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | Innothane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5H5B5K_Innothane-IE-52A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| IE-52A is an elastic Polyether system formulated for hand-batch processing. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA, or TDI. IE-52A is particularly ideal for color-matching due to it's neutral color. |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Cured | 1.09 | g/cm³ | |
| Hardener | 1.09 | g/cm³ | |
| Base Resin | 1.13 | g/cm³ | |
| Molding Shrinkage - Flow | 0.10 to 0.40 | % | ASTM D2566 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 100 Mix Ratio by Weight: 100 | ||
| Resin | Mix Ratio by Weight: 40 Mix Ratio by Volume: 38 | ||
| Demold Time | 720 to 1200 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.075 | Pa·s | |
| 25°C 2 | 0.80 | Pa·s | |
| 25°C 3 | 1.4 | Pa·s | |
| Curing Time 4 | 40 | hr | |
| Gel Time | 20 to 30 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 45 to 55 | ASTM D2240 | |
| Tensile Strength | 6.21 | MPa | ASTM D638 |
| Tensile Elongation at Break | 520 | % | ASTM D638 |
| Tear Strength | 21.0 | kN/m | ASTM D624 |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | Mixed |
| 3 . | Hardener |
| 4 . | 24 hours at 77°F + 16 hours at 150°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| CGPC PVC R-10X MI Bottle Blowing | China General Plastics Corporation | PVC, Flexible | CGPC PVC |
| Formolene® L42009H | Formosa Plastics Corporation, U.S.A. | LLDPE | Formolene® |
| KumhoSunny PBT/ABS HBG5723FR | Shanghai KumhoSunny Plastics Co., Ltd. | ABS+PBT | KumhoSunny PBT/ABS |
| OTECH TPO OTO9097 - Cord Jacket | OTECH Corporation | TPO | OTECH TPO |
| ALCOM® PA66 910/1 AR20 | ALBIS PLASTIC GmbH | Nylon 66 | ALCOM® PA66 |