Borstar® HE6062

Category:	HDPE , High Density Polyethylene
Manufacturer:	Borealis AG
Trademark:	Borstar®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	5GorVl_Borstar-HE6062.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Borstar HE6062 is a black high density (HD) jacketing compound, which is produced with the Borealis proprietary
Borstar bimodal process technology.

Borstar technology allows the manufacturing of polymers outside the traditional MFR and density range making it possible to optimize processability, reduce shrinkage and yet provide excellent physical toughness and environmental stress crack resistance (ESCR).

Borstar HE6062 contains 2.5% well-dispersed carbon black in order to ensure excellent weathering resistance.

General Information
Additive	Carbon black (3%)
Features	Moisture resistance High ESCR (Stress Cracking Resistance) Good UV resistance Workability, good Good wear resistance Scratch resistance Good weather resistance Good toughness Low shrinkage High hardness
Uses	Communication Cable Jacketing Cable sheath Wire and cable applications
Agency Ratings	ASTM D 1248, III, Class C, Cat. 4 Grade E8, E9, J4, W8,9 DIN VDE 0207 Type 2YM3 DIN VDE 0818 EN 187105 EN 50290-2-24 HD 603 S1 DMP 1, 2, 5, 7, 8 HD 620 S2 Part 1, table 4B, DMP 2, 8-12, 14-15, 17 HD 632 S1 ST7 IEC 60502-2 Type ST7 IEC 60708 IEC 60794 IEC 60840 Type ST7 ISO 1872 PE KCHL 45D006 UL I oil grade UL II Oil Rating
Appearance	Black
Processing Method	Extrusion

Physical	Nominal Value	Unit	Test Method
Density			ISO 1183
-- ¹	0.946	g/cm³	ISO 1183
-- ²	0.958	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR)			ISO 1133
190°C/2.16 kg	0.50	g/10 min	ISO 1133
190°C/5.0 kg	2.0	g/10 min	ISO 1133
Environmental Stress-Cracking Resistance ³(Condition B, 50°C, 10% Igepal, F0)	> 5000	hr	IEC 60811-4-1/B

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness
Shaw D, 1 sec	61		ISO 868
Shaw D, 3 seconds	60		DIN 53505

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Yield)	33.0	MPa	ISO 527-2/50
Tensile Strain (Break)	1000	%	ISO 527-2/50
Flexural Modulus	1000	MPa	ASTM D790

Thermal	Nominal Value	Unit	Test Method
Brittleness Temperature	< -76.0	°C	ASTM D746

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	1.0E+16	ohms·cm	IEC 60093
Dielectric Strength	20	kV/mm	IEC 60243-1

Additional Information	Nominal Value	Unit	Test Method
Pressure Test ⁴(115°C)		%	IEC 60811-3-1

Extrusion	Nominal Value	Unit
Melt Temperature	180 - 190	°C

Extrusion instructions
Preheating: 90°CCooling water: 60°C

Note Message
1 .	Base Resin
2 .	Compound
3 .	No crack
4 .	at high temperature, 6 hrs

Resin Grade	Manufacturer	Category	Trademark
Regis® 6200	Noble Polymers	Polyolefin, Unspecified	Regis®
MORETEC™ 0248CN	Prime Polymer Co., Ltd.	LLDPE	MORETEC™
TRIEL® 5722EM	Samyang Corporation	TPEE	TRIEL®
VECTOR® 4211N	TSRC Corporation	SIS	VECTOR®
Dynacom 501-G20	Dynachem Co. Ltd.	ABS	Dynacom