Infino VB-5400G
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5GSGHS_Infino-VB-5400G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino VB-5400G is a Polybutylene Terephthalate (PBT) product filled with glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.74 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.20 mm | 0.35 to 0.42 | % | |
| Across Flow : 3.20 mm | 0.54 to 0.66 | % | |
| Water Absorption (23°C, 24 hr) | 0.060 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 12000 | MPa | ASTM D638 |
| -- | 13000 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 130 | MPa | ASTM D638 |
| Yield | 165 | MPa | ISO 527-2/50 |
| Break 3 | 150 | MPa | ASTM D638 |
| Break | 165 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 4 | 3.0 | % | ASTM D638 |
| Break | 2.8 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 11000 | MPa | ASTM D790 |
| -- 6 | 14000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 220 | MPa | ASTM D790 |
| -- 8 | 229 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 11 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 88 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 77 | J/m | ASTM D256 |
| 23°C 10 | 10 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 220 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 4.00 mm | 219 | °C | ISO 75-2/B |
| 0.45 MPa, Annealed | 219 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 200 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 201 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed, 4.00 mm | 202 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 204 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-0 | ||
| 3.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 | °C | |
| Desiccant Dryer | 100 | °C | |
| Drying Time | |||
| -- | 4.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 210 to 220 | °C | |
| Middle Temperature | 225 to 230 | °C | |
| Front Temperature | 240 to 250 | °C | |
| Nozzle Temperature | 250 | °C | |
| Mold Temperature | 60.0 to 120 | °C | |
| Injection Pressure | 49.0 to 245 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4 mm |
| 10 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propylux® Unfilled | Westlake Plastics Company | PP, Unspecified | Propylux® |
| VICTREX® PEEK 90HMF40 | Victrex plc | PEEK | VICTREX® PEEK |
| ALCOM® PA6 900/13 GF15 MRX45 | ALBIS PLASTIC GmbH | Nylon 6 | ALCOM® PA6 |
| Gallonprene® GP540-7005 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| KEBAFORM® C 50.0 | BARLOG plastics GmbH | Acetal (POM) Copolymer | KEBAFORM® C |